sterling silver stone set cabochon rings from scrap

DSCF3522

Carved depression into charcoal block

DSCF3524

After melting the scrap, this is the ingot before forging and subsequent milling down to size with rolling mill.

DSCF3525

The moonstone was mine to start with. Paul and Clair at the jewellery workshop Porthleven kindly gave me all the others to play with

DSCF3526

My attempt to try and KISS – keep things simple stupid 🙂

DSCF3528

The shanks were made from 3mm wire, rolled into a semi ‘D’ section. I already had the wire, only the settings were made from scrap.

Wato wato all

Alas I didn’t take a picture of a moonstone ring I made from parts of my disastrous journey into the world of outscoring casting. I had my moon series domes cast in three sizes to make bracelets and earrings. The results were not great.

Going through my scrap bin, I found one of the damaged domes and decided to make a moonstone ring with the moon dome as the setting. I wasn’t overly keen on it, to my mind it was too tall. Reen insisted that she wanted Clair and Paul to take a look, they sold it within a couple of days!!!

I always battle with what will be attractive, taking every effort to try to keep a bit of my personality in a piece the same time. I realise that this a case of mind over matter; People don’t mind cos it don’t matter 😉

Buoyed with this success, I have made these rings as simple as possible, no trace of an individual maker.

Paid work, therefore funds, still being somewhat illusive at this time, I was forced to recycle some scrap to make the bases for the stones and the bezel. Luckily I had some wire, if not I would have had to make a draw plate to make my own. I put the wire through the ‘D’ section of the rollers and partially rounded the ends. I have noticed, around here anyway, most rings in the art jewellery sections appear to use mainly round wire. I think the extra surface area of the inside of a flat shank is more comfortable. Also, the size of the stones used, I think will stop them flopping on a wearers finger.

As you see in the pictures, I used a block of charcoal to make a depression, doubling as a crucible and mould at the same time. I’m not sure as the wisdom of this, the amount of heat it took was, to me, disproportionate to the amount of scrap in the hole. I can only surmise the block took away much of the heat. For the second batch I used a crucible, it was faster. The reason I wanted to melt into the charcoal was for the reducing effect. The carbon, when heated, takes away/uses up the oxygen, less fire-stain as the ingot cools in a much reduced atmosphere.

Fingers crossed this could be a far more productive avenue for me to potentially take in future. I feel bound to say, if you wish to inject some of your personality into your work, you may need to consider if your personality is attractive enough to share. This is a lesson I am learning. I was looking through my library of books and came across; Silversmithing a basic manual by Nicholas D Humez ISBN 0-316-38151-9. I wish to share with you a passage written there that made me think, perhaps it will do so for you also;-

Third, a word about attitude,or where your head is at. When you sit down at the workbench, if you are not prepaired to commit yourself to being all there – not thinking about lunch, or where your rent is coming from, or why so-and-so is peeved at you, or even how groovy you are sitting at this workbench – you are doing yourself and the metal no favour and will probably botch the job in front of you, possible exposing yourself to danger as well, should your torch or buffing wheel malfunction. Similarly, if you are furious at the world and take it out on the silver, your problems will not go away and your work will probably lack subtlety, even if your aim is good. And if you are just plain sloppy, your work will show it, and in a soberer moment you will be ashamed to have wasted your bench time so. To a certain extent, you will smith silver with the same style with which you run the rest of your life; hence “cleaning up your act” on the bench – that is, trying to do as good a job of being a silversmith as you know how – will work or not according to how well you are coping with the world outside the workshop. Don’t hope to do your best piece of the day after your cat dies: it is simply too much to expect of yourself.

Wow, wisdom and not more than a little kick from 1976. Now I know where I’m going wrong. Time to make more plain work I think 🙂

Until next time, very best wishes.

Stu Art

 